CORROSION ENGINEERING SCIENCE AND TECHNOLOGY
卷 40, 期 4, 页码 337-343出版社
TAYLOR & FRANCIS LTD
DOI: 10.1179/174327805X66326
关键词
magnesium; crystallographic pitting; corrosion filaments; single crystal; corrosion; dichromate; hcp metals
The corrosion behaviour of three low index planes of an hcp magnesium (Mg) single crystal was investigated in 10(-2) M NaCl/10(-4) M dichromate solution. The Mg ( 0001) surface exhibited pitting corrosion susceptibility at the open circuit potential. However, the (10 (1) over bar0), and (11 (2) over bar0) surfaces were passive at open circuit and pitting only initiated at potentials slightly anodic to their open circuit potentials. The onset of stable dissolution in the three surfaces was marked by the formation and propagation of corrosion filaments. For the three surfaces investigated, pit shape was non-geometric, however, pit propagation was generally found to occur along preferential crystallographic directions. An analysis of the preferred crystallographic directions is presented.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据