MACROMOLECULAR MATERIALS AND ENGINEERING
卷 290, 期 12, 页码 1157-1165出版社
WILEY-V C H VERLAG GMBH
DOI: 10.1002/mame.200500163
关键词
composites; mechanical properties; polyesters; processing; thermal properties
Hydroxyapatite, chitosan, and aliphatic polyester were compounded using a twin-screw extruder. The polyesters include poly(epsilon-caprolac tone) (PCL), poly(lactic acid), poly(butylene succinate) (PBS), and poly(butylene terephthalate adipate). The mass fraction of chitosan ranged from 17.5 to 45%, while that of HA ranged from 10 to 30%. These blends were injection molded and evaluated for thermal, morphological, and mechanical properties. The addition of hydroxyapatite decreased the crystallinity in chitosan/PBS blends, while in blends containing chitosan/PCL, the crystallinity increased. Addition of hydroxyapatite significantly decreased the tensile strength and elongation of polyester/hydroxyapatite composites as well as chitosan/polyester/hydroxyapatite composites with elongations undergoing decreases over an order of magnitude. The tensile strength of the composite was dictated by the adhesion of HA to the chitosan/polyester matrix. The tensile strength of composites containing hydroxyapatite could be predicted using the Nicolai and Narkis equation for weak filler adhesion (K approximate to 1.21). Tensile-fractured and cryogenically-fractured surface indicates extensive debonding of hydroxyapatite crystals from the matrix, indicating weak adhesion. The adhe-sion of hydroxyapatite was higher for pure polyester than those containing chitosan and polyester. The modulus of the composites registered modest increase. The two main diffraction peaks observed using WAXS are unaffected by the amount of chitosan or hydroxyapatite.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据