APPLIED CATALYSIS A-GENERAL
卷 298, 期 -, 页码 40-49出版社
ELSEVIER
DOI: 10.1016/j.apcata.2005.09.017
关键词
supported catalysts beta-NiMoO4 i-butane; i-butene; oxidative dehydrogenation; nanostructure; TPR; CO2-TPD; NH3-TPD; SEM-EDS; TEM-EDX
NiMoO4 silica-supported samples (6.5% w/w) were prepared by coprecipitation technique. In order to study the influence of the surface area of the support material, silicas with different surface areas have been used: Durosil (60 m(2)/g) and Sipernat 22 (190 m(2)/g) from Degussa and silica prepared in the laboratory (590 m(2)/g). Nanosized grains of beta-NiMoO4 phase were obtained for all the prepared samples. The crystallinity of the active phase (mixed oxide) depends on the nature of the support material. The laboratory-made silica allowed reaching the highest degree of nanocrystallinity (observed by TEM) for the active phase. Results from TPR and ITR show that the sample reducibility depends on the size and crystallinity of the dispersed active phase. All the prepared samples were more reducible than the unsupported NiMoO4 sample due to the presence of P-phase instead alpha-NiMoO4 phase. In the tested conditions the sample prepared using the silica with the highest surface area displays the highest i-butane conversion, the highest i-butene selectivity and the lowest selectivity towards deep oxidation products. (c) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据