关键词
copper-nickel alloy; nanocrystallites; microemulsion
The well-mixed copper-nickel nanoparticles were prepared when the molar ratio of Cu2+ to Ni2+ was 1:1 by simultaneous reduction Of CuSO4 and NiCl2 with hydrazine in the microemulsion of SIDS/n-butanol/n-heptane/water at 70 degrees C, and was characterized by TEM, ED, TGA, EDS, and XRD. ED analysis and XRD patterns suggest the formation of the homogeneous alloy structure in the bimetallic nanoparticles. Average size of the sample calculated from the full width at medium height of peak I I I in the XRD patterns using Scherrer formula is 5.53 nm. TEM photographs show a narrow distribution of Cu-Ni nanoparticles that essentially are monodispersed and the mean diameter is 12 nm. The results indicate that the composition and size of alloy nanoparticles depend on the mole ratio of H2O to SDS, the method of addition of Cu2+ and Ni2+, and the mole ratio of Cu2+ and Ni2+ in the initial precursor solution. (c) 2005 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据