PHYSICA B-CONDENSED MATTER
卷 371, 期 1, 页码 187-191出版社
ELSEVIER
DOI: 10.1016/j.physb.2005.10.110
关键词
La1-xCexMnO3; oxygen content; transport properties; metal-semiconductor transition
Effects of oxygen content oil the transport property of the La0.7Ce0.3MnO3+delta film, which was believed all electron-doped manganite, have been experimentally studied. The content of oxygen of the film was modified by repeatedly annealing the film in vacuum at various temperatures between 200 and 550 degrees C, and the resistivity was measured as a function of temperature after each annealing. The film was hole-doped when it was oxygen rich, and a metal-to-semiconductor transition (MST) was found. With the decrease of the oxygen content, the MST temperature decreased, and finally the MST vanished, and the resistivity increased overall. The sample showed semiconductive behaviors, when it was true electron-doped (average valence of Mn less than 3+). The results imply that the magnetic and transport behaviors and strong magnetic-resistive correlation in La0.7Ce0.3MnO3+delta film result from the interaction between Mn3+ and Mn4+. (c) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据