SOLID STATE COMMUNICATIONS
卷 137, 期 6, 页码 315-319出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ssc.2005.11.037
关键词
HgTe nanoparticles; trap-mediated hopping process; photocurrent; photoluminesence
Absorption, photoluminescence (PL), photoresponse, and I-V measurements were made for a close-packed HgTe nanoparticle film without organic capping materials to investigate its optoelectronic characteristics in the infrared (IR) range. In the absorption and PL spectra taken for the close-packed nanoparticle film, the wavelength of exciton peak was red-shifted, compared with 1-thioglycerol capped HgTe nanoparticles dispersed in solution. For the HgTe nanoparticle film, dark current was below several pA level, current was increased by about three orders of magnitude at a biased voltage of 3 V under the illumination, and photoresponse was very rapid compared with 1-thioglycerol capped HgTe nanoparticles. These optoelectronic characteristics illustrate that HgTe nanoparticles are one of promising materials for the photodetector in the IR range. Finally, the origin for the increase of photocurrent with increasing temperature observed in this study will be discussed. (c) 2005 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据