MICROPOROUS AND MESOPOROUS MATERIALS
卷 89, 期 1-3, 页码 33-38出版社
ELSEVIER
DOI: 10.1016/j.micromeso.2005.06.045
关键词
nickel(II) ferrite; oxalates; porosity; silica coating; BET method
The porosity of co-precipitated iron(II) and nickel(II) oxalate samples was investigated after thermolysis at different temperatures. Specific surface area values of the obtained nickel(II) ferrite samples have been determined by means of the BET method. Maximal values of the specific surface area and pore volume have been fixed for ferrite samples obtained when the thermolysis of oxalates was carried at 500 degrees C during an hour. Specific surface value in this case was 335 m(2)/g and pore volume 0.46 cm(3)/g. At comparatively higher temperatures of thermal decomposition (600 degrees C) the indicated parameters of porous structure decrease sharply: specific surface area value to 20-25 m(2)/g and pore volume - to 0.20 cm(3)/g. A similar picture observed also when thermolysis was carried at 500 degrees C during 2 h. In this case specific surface area value decreases to 30 m(2)/g and pore volume - to 0.22 cm(3)/g. (c) 2005 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据