MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 420, 期 1-2, 页码 322-332出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2006.01.092
关键词
ZK60-Y; magnesium alloy; precipitate; age hardening
This paper investigated the influence of the microstructure on the mechanical properties of the forged ZK60-Y alloy under different heat treatments (T-4, T-5 and T-6). The results show that the alloy at the direct artificial ageing treatment has superior strength and plasticity. X-ray analysis, SEM fracture observation and EDAX spectrum analysis reveal that bulk w-Mg3YZn3 and coarsened rod-like MgZn'(beta(1)',) phases have great influence on the tensile properties of the alloy. Further investigations of the alloy aged at 180 degrees C, 200 degrees C and 225 degrees C for 0.5-100 h, respectively, suggest that the mechanical properties and the fracture characteristics are closely related with the variation of the rod-like beta(1)', precipitation. The fracture observation of the samples aged at 200 degrees C indicates that with the increase of the density and the size of the rod-like beta(1)', precipitation, more semi-cleavage planes will appear on the fracture surfaces. (c) 2006 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据