期刊
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN
卷 114, 期 1328, 页码 303-307出版社
CERAMIC SOC JAPAN-NIPPON SERAMIKKUSU KYOKAI
DOI: 10.2109/jcersj.114.303
关键词
proton conduction; composite electrolyte; self-assemble method mesoporous material; fuel cell
Silica mesoporous structures incorporated with phosphorus were prepared and their proton conductivity was evaluated at temperatures of up to 150 degrees C under saturated or controlled water vapor pressure. The fixing of phosphoric acid through heat treatment after forming the mesostructure had a limited effect on the improvement in proton conductivity only in a relatively low-temperature region. The incorporation of phosphorus during mesoporous silica formation decreased the surface area but was effective in improving proton conductivity. A sample with a low P/Si atomic ratio of 0.07 showed the highest proton conductivity above 10(-2) Scm(-1) at 100 to 120 degrees C under saturated water vapor pressure. A sample with a high P/Si atomic ratio of 0.25 showed relatively high conductivities being maintained even at low relative humidity at 150 degrees C. An adequate phosphorus concentration and a large surface area were found necessary for high and humidity-independent proton conductivity in mesoporous silica.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据