nanocystalline; grain size; corrosion behavior; passive film
Fe-10Cr nanocrystalline (nc) coatings with a grain size of 20-30 nm were synthesized on glass substrates by magnetron sputtering. The corrosion behavior was investigated in 0.05 mol/L H2SO4 + 0.25 mol/L Na2SO4 and 0.05 mol/L H2SO4 + 0.5 mol/L NaCl solution by polarization curves, EIS and Mott-Schottky analysis. The results showed that compared to Fe-10Cr cast alloy, the active dissolution of the coating was accelerated; the passive film contained more Cr and therefore the coating was easier to passivate. The passive films formed on Fe-10Cr nc and cast alloy exhibited n-type semiconducting behavior in acidic solutions without Cl- and p-type semiconducting behavior in acidic solutions with Cl-. The lower breakdown potential for both materials in the solution with Cl- is related to the p-type passive film formed on them. For Fe-10Cr nc, lower donor density and increased Cr content were responsible for the chemical stability of the passive film. (c) 2005 Published by Elsevier Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据