Commercially pure titanium (cpTi) was etched using three concentrated acids: 18% HCl, 43% H3PO4, and 48% H2SO4. The bond strengths between five types of veneering composite resin and eight cpTi treatments (involving combinations of sandblasting, acid etching in 48% H2SO4, and vacuum firing) were determined before and after 10,000 and 20,000 thermal cycles. There were no significant differences in the bond strength of resin to cpTi after etching in 48% H2SO4 at 90 degrees C for 15 minutes, at 60 degrees C for 15, 30, or 60 minutes, and after sandblasting with and without vacuum firing (p>0.05); moreover, these treatments yielded the highest values. As for vacuum firing, it had no significant effect on resin bond strength to cpTi before or after 10,000 and 20,000 thermal cycles. We therefore concluded that acid etching in concentrated H2SO4 is a simple and effective surface modification method of titanium for bonding to veneering composite resins.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据