Synthesis and characterization of nanosilica/polyacrylate composite latex

The nanosilica/polyacrylate organic-inorganic composite latex was synthesized by in-situ emulsion polymerization of methyl methacrylate (MMA) and butyl acrylate (BA) in the presence of silica nanoparticles, which were modified by silane coupling agent. The surface properties and dispersibility of silica nanoparticles modification, chemical structure, Zeta potential, diameter distribution of the composite latex prepared, surface roughness, and thermal stability of the hybrid film formed by the composite latex were investigated by fourier transform infrared spectrometer (FTIR), transmission electron microscopy (TEM), Zeta meter, ZetaPlus apparatus (dynamic light scattering method), atomic force microscopy (AFM), and thermogravimetric analysis (TGA), respectively. After modification with silane coupling agent, silane was grafted onto the surface of silica nanoparticles to form the organic layers, which was able to efficiently prevent the silica nanoparticles from aggregating to individually homogeneous disperse in the in-situ emulsion polymerization system and improve the compatibility of silica nanoparticles with the acrylate monomers. The nanosilica/polyacrylate organic-inorganic composite latex prepared had the properties of silica nanoparticles and pure polyacrylate latex but was not simply a combination. Strong chemical bonding tethered the silica and acrylate chains to form the core/shell structural composite latex. Consequently, the hybrid film formed by nanosilica/polyacrylate composite latex exhibited a smooth surface and better thermal properties than the pure polyacrylate film.