Electrospinning of nylon-6,66,1010 terpolymer

Ultrafine nylon fibers were prepared by electrospinning of nylon-6,66,1010 terpolymer solution in 2,2,2-trifluoroethanol (TFE). The morphology, crystallinity and mechanical properties of the electrospun nylon-6,66,1010 fibers were investigated by scanning electron microscope (SEM), differential scanning calorimetry (DSC), wide angle X-ray diffraction (WAXD) and tensile test. The effects of electrospun process parameters such as solution concentration, voltage and tip-to-collector distance on the morphology and the average size of the electrospun fibers were also studied. The results show that the spinnable concentration of nylon-6,66, 1010/TFE solution is in the range of 6-14 wt%, and higher solution concentration favors the formation of uniform fibers without beads. The diameters of the electrospun fibers increase with increasing the solution concentration and decrease slightly with increasing the voltage and needle tip-to-collector distance. But no obvious morphology changes were found with the increase of the voltage and collection distance. DSC and WAXD results suggest that the electrospun nylon-6,66,1010 membranes have lower crystallinity than those of the corresponding casting films. The electrospun nylon-6,66,1010 membrane obtained from the 14 wt% concentration exhibits the largest tensile strength and elongation at break. (c) 2006 Elsevier Ltd. All rights reserved.