JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 303, 期 2, 页码 309-317出版社
ELSEVIER
DOI: 10.1016/j.jmmm.2006.01.106
关键词
FePt; perpendicular media; strain; underlayer
A method based on strain-induced phase transformation was used to lower the ordering temperature of FePt films. The strain resulted from the lattice mismatch between the FePt film and the substrate or underlayer favored the ordering. The relationships between the lattice mismatch, the ordering of FePt film, and the corresponding magnetic anisotropic constant were investigated. A critical lattice mismatch near 6.33% was believed to be most suitable for improving the chemical ordering of the FePt films. CrX (X = Ru, Mo, W, Ti) alloys with (2 0 0) texture was used to control the easy axis and ordering temperature of FePt films on glass substrate. Large uniaxial anisotropy constant K-&u >= 1 x 10(7) erg/cm(3), good magnetic squareness (similar to 1) and FePt(001) texture (rocking curve -5 degrees) were obtained at the temperature T-s >= 250 degrees C when using CrRu underlayer. The diffusion from overlying layers of Ag and Cu and an inserted Ag pinning layer were effective in reducing the exchange decoupling and changing the magnetization reversal. The media noise was effectively reduced and the SNR was remarkably enhanced when a 2 nm Ag was inserted. (C) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据