Precipitation induced densification in a sintered Al-Zn-Mg-Cu alloy

It is demonstrated that slow cooling to 200 degrees C from a high sintering temperature (620 degrees C) reduces porosity in an Al-8Zn-2.5Mg-1Cu powder compact when compared to isothermal sintering at the higher temperature for a longer time. The reduction in porosity is attributed to shrinkage associated with removal of solute from the aluminium solid solution and heterogeneous precipitation of the eta phase (MgZn2), particularly onto pore surfaces. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.