JOURNAL OF COLLOID AND INTERFACE SCIENCE
卷 300, 期 1, 页码 219-224出版社
ACADEMIC PRESS INC ELSEVIER SCIENCE
DOI: 10.1016/j.jcis.2006.03.060
关键词
dysprosium oxide; mesoporous material; nanocrystal; surfactant template; sol-gel process
A simple route of combined sol-gel process with surfactant-assisted templating technique was successfully employed for the first time to synthesize nanocrystalline mesoporous Dy2O3 with narrow monomodal pore size distribution under mild conditions. The nanocrystalline Dy2O3 with monomodal mesoporous characteristic was ultimately achieved by controlling the hydrolysis and condensation steps of dysprosium n-butoxide modified with acetylacetone in the presence of laurylamine hydrochloride surfactant aqueous solution. The synthesized material was methodically characterized by thermogravimetry and differential thermal analysis (TG-DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), selected-area electron diffraction (SAED), N-2 adsorption-desorption, Brunauer-Emmett-Teller (BET) surface area analysis, and Barrett-Joyner-Halenda (BJH) pore size distribution analysis. The particle size of the synthesized Dy2O3 in nanosized range obtained from the SEM and HRTEM micrographs was in good accordance with the crystallite size estimated from the XRD result. The N-2 adsorption-desorption result exhibited hysteresis pattern with single loop, indicating the existence of monomodal mesopore. The extremely narrow pore size distribution with mean pore diameter in the mesopore region of the synthesized Dy2O3 was also confirmed by the BJH result. (c) 2006 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据