SURFACE & COATINGS TECHNOLOGY
卷 200, 期 24, 页码 6690-6695出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2005.10.006
关键词
PEEK coating; flame spray; annealing; crystallization; hardness; tribological behavior
An amorphous PEEK coating was prepared on an At substrate by a flame spraying process. The amorphous coating was subjected to an annealing treatment under an annealing temperature from 180 to 300 degrees C and a holding time from 1 to 30 min. The cold crystallization behavior of the as-sprayed coating differential scanning calorimetry (DSC) and wide angle X-ray diffraction (WAXD) measurements. The hardness and tribological behavior of the coatings were investigated. Both DSC and WAXD analysis revealed that the annealed coatings exhibited a semicrystalline structure. Coexistence of double crystal entities in annealed coatings was deduced. The annealed coatings exhibit higher hardness, lower friction coefficient and wear rate. Both the annealing temperature and holding time can benefit the coating hardness. The annealing condition in the studied range has little influence on the tribological behavior of the coatings. The variances of the coating mechanical properties were correlated with the modifications of the coating structures induced by the annealing treatments. (c) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据