JOURNAL OF MEMBRANE SCIENCE
卷 279, 期 1-2, 页码 230-237出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.memsci.2005.12.009
关键词
polysulfone; PEG additive; rheological and thermodynamic variation; kinetics parameter; kinetics of membrane formation
In order to clarify the mechanism through which poly(ethylene glycol) (PEG) can affect the kinetics of membrane formation, phase-inversion process was used in membrane preparation from polysulfone (PSF) casting solution with PEG introduction. The rheological and thermodynamic variation in PSF solution by PEG introduction was investigated by using the method of viscosity measurement and triangle phase diagram. It was found that PEG addition could work in favor of enhancement thermodynamically and hindrance theologically in PSF solution demixing. With the increase of temperature, the viscosity of PSF casting solution decreased and the miscibility of PSF solution with non-solvent increased. On the basis of the relationship between wet membrane thickness and coagulation time, a new method used to calculate kinetics parameter (D-a) Of membrane formation was founded and an equation of D-a = d(2)/t was established. With the increase of PEG concentration, it was revealed that D-a increased firstly and then decreased with a maximum value of 0.001428 mm(2)/s at certain temperature (20 degrees C). With the increase of coagulation bath temperature, Da increased continuously when the composition of casting solution was constant. D-a was mainly influenced by the surface morphology of membrane and the thermodynamic, rheological properties of casting solution. (c) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据