SCRIPTA MATERIALIA
卷 55, 期 4, 页码 399-402出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.scriptamat.2006.03.062
关键词
nickel aluminide; thermornechanical processing; nanostructure; tensile properties; fracture
Fully dense nanocrystalline Ni3Al intermetallic foil was successfully produced from as-cast coarse-grained sheet by heavy rolling at liquid nitrogen temperature and subsequent recrystallization. The mechanical properties and fracture behavior of the nanocrystalline foil with grain size about 20 nm were derived from uniaxial tension tests at room temperature. Typically, the nanocrystalline foil exhibits significantly higher yield strength (similar to 2.6 GPa), and reduced tensile elongation (similar to 4.0%) relative to its microcrystalline counterpart (yield strength similar to 0.7 GPa and tensile elongation similar to 22%). (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.