hot target; low pressure; reactive sputtering; thin film; titanium oxide
Thin films of TiO2 were deposited onto (1 0 0) oriented silicon and glass substrates using modified magnetron sputtering method. The method,, among the others, consisted in employing low pressure of reactive gas (< 10(-1) Pa), hot target (additional heating of the target) and low deposition rate (about 0.1 nm/s). X-ray diffraction, X-ray photoelectron spectroscopy and optical transmission measurements have been applied to Study the influence of film thickness, substrate type and post annealing process oil the microstructure, composition, and optical properties of prepared thin films. It was found that the lattice spacings were a bit smaller than those of bulk material what indicated the contraction of the thin film. Optical examinations have shown that the fundamental absorption edge was shifted toward longer wavelength region (from 330 to 351 nm) as the thickness of the film increased. It was stated that thin films of TiO2 were almost stoichiometric after additional annealing.. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据