Strategies for the preparation of carboranyl-containing hybrid materials by hydrolytic sol-gel process were investigated with carboranyl-containing poly-trialkoxysilyl precursors: 1,2-[(CH2)(3)Si(OEt)(3)](2)-1,2-C2B10H10 (P1) and 1-R-2-Si[(CH2)(2)Si(OEt)(3)](3)-1,2-C2B10H10(R)Me, P2 or Ph, P3). When P1 is used, the integrity of the precursor is preserved whatever is the catalyst (F-, H+), while for P2 and P3, cleavage of the C-cluster-Si bond is observed with F- and OH- as catalysts. Such Si-C-cluster bond cleavage leads to porous hybrid materials templated by the carborane, which is further eliminated from the material and totally recovered. In contrast, nonporous materials are obtained when carborane is preserved in the materials. Part of this hybrid material exhibits a lamellar structure in relation to the presence of the carborane units. In dry air, high thermal stability is observed for such materials and results in a very limited oxidation of the material at 1200 degrees C ( weight gain of < 5%). In an inert atmosphere, high thermal stability combined with several chemical transformations leads to a limited weight loss, graphitization, and oxide and under-oxide mixtures. Materials were characterized by IR, solid-state NMR (Si-29, C-13), porosimetry, X-ray diffraction, SEM, TEM, TGA, and XPS.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据