期刊
JOURNAL OF NON-CRYSTALLINE SOLIDS
卷 352, 期 32-35, 页码 3729-3733出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnoncrysol.2006.03.103
关键词
catalysis; nanocrystals; electrochromics; X-ray diffraction; defects; powders; nanoparticles; sintering
Nanoparticles of fcc-NiO phase were obtained by heating the dried resin resultant of a mixture of gelatin and NiCl2 center dot 6H(2)O in aqueous solution. The average particle size and microstrain were calculated from the line broadening of X-ray powder diffraction peaks, and these values were between 15 nm and 78 nm, and 0.056% and 0.172%, respectively. The Rietveld refinement method was applied to all diffraction patterns. The particle size, obtained from this procedure, changes as a function of temperature, heating time and the remarkable reduction due to the addition of NaOH to the solution, which can be attributed to the presence of NaCl crystals and carbon encapsulating NiO nanoparticles during the heating. The heating temperature was in the range of 350-700 degrees C. Thermo-gravimetric analysis showed that the majority of organic fraction starts to disappear after 300 degrees C. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据