JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY
卷 183, 期 1-2, 页码 171-175出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jphotochem.2006.03.013
关键词
TiO2 photocatalysis; nitrogen doping; NH3/Ar plasma
NH3(10%)/Ar plasmas were generated at different gas pressures in a mechanical milling chamber, and were uniformly irradiated on an anatase TiO2 powder with 300 m(2)/g of which corresponding diameter was 7 nm. Crystal structures of the plasma irradiated powders were the same as that of the raw powder, regardless of the gas pressure. On the other hand, the optical property of the resultant powders was varied with regard to the gas pressure. When plasma generated and irradiated at 300 Pa, the powder had the specific surface area (SSA) of 283 m(2)/g and noticeable absorption in vis light range was observed. In addition, the powder showed an improvement of the photocatalytic oxidation activity of CH3CHO under vis light. These results indicated that the present plasma treatment is capable of modifying TiO2 nanopowder for improving photoactivity without large SSA reduction, which is often seen in the modification with annealing. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据