Degradation behavior of membrane-electrode-assembly materials in 10-cell PEMFC stack

A 10-cell proton exchange membrane fuel cell (PEMFC) stack with single-cell active area of 4cm(2) was constructed to investigate the degradation behavior of membrane-electrode-assembly materials under condition of ambient humidity. The stack had been tested for 200h with H-2/ambient-humidity air (20-25% RH and 18-22 degrees C), ambient pressure and 60 degrees C. The 200h performance introduces an obvious decay to the Pt/catalyst compared to the decay of the PEMs. The Pt nanoparticles have serious physical aggregation after the 200h performance without crystal lattice change. Oxygen reduction potential of the Pt/C catalyst considerably decreased from similar to 0.48V vs. SCE to similar to 0.4 V. The loss of the Pt particles is more rapid than the carbon supports in the catalyst layer and the reason is most likely that the platinum is missed as metal particles when the contact carbon layer has been corroded. The PEMs also have degradations in proton conductivity and many of F-elements dissociate from the perfluorocarbon chains. (c) 2006 International Association for Hydrogen Energy. Published by Elsevier Ltd. All rights reserved.