Confinement, composition, and spin-coating effects on the glass transition and stress relaxation of thin films of polystyrene and styrene-containing random copolymers: Sensing by intrinsic fluorescence

The glass transition temperatures (T(g)s) of polystyrene (PS) and styrene/methyl methacrylate (S/MMA) random copolymer films are characterized by intrinsic fluorescence, i.e., monomer fluorescence from an excited-state phenyl ring and excimer fluorescence from an excited-state dimer of two phenyl rings. The T-g is determined from the intersection of the rubbery- and glassy-state temperature dependences of the integrated fluorescence intensity measured upon cooling from an equilibrated state. With PS, the effects of nanoconfinement on T-g and the transition strength agree with results from studies using probe fluorescence and ellipsometry. The T-g-nanoconfinement effect is tuned by copolymer composition. As S-content is reduced from 100 mol% to 22 mol%, the confinement effect changes from a reduction to an enhancement of T-g relative to bulk T-g. Intrinsic fluorescence is also a powerful toot for characterizing relaxation of residual stresses. Stresses induced by spin coating affect local conformations, which in turn affect excimer and monomer fluorescence and thereby integrated intensity. The heating protocol needed to achieve apparently equilibrated local conformations is determined by equivalence in the integrated intensities obtained upon heating and subsequent cooling. While partial stress relaxation occurs upon heating in the glassy state, full relaxation of local conformations requires that a film be heated above T-g for times that are long relative to the average cooperative segmental relaxation time. For example, in thin and ultrathin films, equilibration is achieved by heating slowly (similar to 1 K/min) to 15-20 K above Tg. Dilute solution fluorescence of PS and S/MMA copolymers is also characterized and compared to reports in the literature. (c) 2006 Published by Elsevier Ltd.