JOURNAL OF POWER SOURCES
卷 161, 期 1, 页码 730-736出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2006.03.074
关键词
mesoporous carbon; carbon electrodes; supercapacitors; nanostructure; electrochemical properties
Symmetrical carbon/carbon double layer capacitors (EDLCs) were fabricated employing nanostructured mesoporous nongraphitized carbon black (NMCB) powders and their EDLC behavior was studied using electrochemical techniques viz., cyclic voltammetry, a.c.-impedance, and constant current cycling. Rectangular shape cyclic characteristics were observed indicating the double layer behavior of the NMCB carbon electrodes. The mechanism of double layer formation and frequency dependent capacitance were deduced from the ac-impedance analysis. Specific capacitance, power density and energy density were derived from constant current charge/discharge measurements. NMCB powders demonstrated a specific capacitance of about similar to 39 Fg(-1) and the power density of 782W kg(- 1) at a current density of 32mA cm(-2). Nevertheless, at a low current density (3 mA cm(-2)), the specific capacitance of similar to 44 F g(-1) was achieved, which corroborates with the values obtained by means of ac-impedance (40 F g(-1)) and cyclic voltammetry (41.5 F g(-1)). The test cells demonstrated the stable cycle performance over several hundreds of cycles. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据