期刊
THIN SOLID FILMS
卷 515, 期 2, 页码 674-677出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.tsf.2005.12.243
关键词
TiO2; spray pyrolysis; structure; electrical properties
The sot-gel spray pyroiysis method was used to grow TiO2 thin films onto silicon wafers at substrate temperatures between 315 and 500 degrees C using pulsed spray solution feed followed by annealing in the temperature interval from 500 to 800 degrees C in air. According to FTIR, XRD, and Raman, the anatase/rutile phase transformation temperature was found to depend on the film deposition temperature. Film thickness and refractive index were determined by Ellipsometry, giving the refractive indexes of 2.1-2.3 and 2.2-2.6 for anatase and rutile, respectively. According to AFM, film roughness increases with annealing temperature from 700 to 800 degrees C from 0.60 to 1.10 nm and from 0.35 to 0.70 nm for the films deposited at 375 and 435 degrees C, respectively. The effective dielectric constant values were in the range of 36 to 46 for anatase and 53 to 70 for rutile at 10 kHz. The conductivity activation energy for TiO2 films with anatase and rutile structure was found to be 100 and 60 meV, respectively (c) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据