期刊
SOLID STATE IONICS
卷 177, 期 26-32, 页码 2347-2351出版社
ELSEVIER
DOI: 10.1016/j.ssi.2006.05.043
关键词
strontium zirconate; strontium titanate; HRTEM; STEM-EDS; proton conductivity
Superlattice thin films of a perovskite-type oxide proton conductor SrZ(r0.95)Y(0.05)O(3)/SrTiO3 were fabricated and their structural and electrical properties were investigated. X-ray and electron diffraction analysis reveals that the thin films were epitaxially gown on MgO (001) substrate. High-resolution transmission electron microscopy observation shows that the multilayered structure is uniform and that the interfaces between the different layers are of low roughness. Misfit dislocations are found at the interface, having Burgers vectors in direction a[100]. From the local elemental analysis, the interdiffusion of Zr and Ti between layers was not observed, while Mg impurities diffused from the substrate are observed. The in-plane electrical conductivity of the thin films was measured by impedance spectroscopy. The conductivity of the superlattices shows a higher value than a single SrZr0.95Y0.05O3 film. The activation energies of the epitaxial layers show relatively higher value than the corresponding single crystal. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据