The cutting of multi-walled carbon nanotubes and their strong interfacial interaction with polyamide 6 in the solid state

The cutting of multi-walled carbon nanotubes (MWCNTs) using solid state shear milling ((SM)-M-3) method and their strong interfacial interaction with polyamide 6 (PA6) in the solid state were studied. Transmission electron microscopy showed that after milling, the CNTs were greatly reduced in length, and disentangled, being straighter with open ends. Fourier transform infrared spectra and differential scanning calorimeter analysis indicated the existence of strong interfacial interactions between MWCNTs and PA6 of the pan-milled PA6/CNTs powder. It was further quantified by thermogravimetric analysis that about 30 wt.% of PA6 formed a strong combining force with CNTs after pan-milling. The mechanism of cutting CNTs and the reason for their strong interfacial interactions with PA6 in the solid state were discussed. A fine and homogeneous dispersion of CNTs throughout PA6 matrix was observed by scanning electron microscopy. The tensile properties of the composites prepared by the S3M method were significantly improved compared to those of pure PA6 and composites prepared by conventional melt mixing. Upon incorporation of only 1.5 wt.% MWCNTs, the tensile modulus of PA6 was enhanced from 2448 MPa to 4439 MPa, by about 80%, and the tensile strength was increased by about 23%. (c) 2006 Elsevier Ltd. All rights reserved.