POLYMER DEGRADATION AND STABILITY
卷 91, 期 11, 页码 2554-2559出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2006.05.009
关键词
block copolymers; poly lactide; poly ethylene glycol; degradation; nanoparticles
Diblock copolymers composed of poly(oxy-ethylene) (POE) and poly(DL-lactic acid) segments were synthesized by anionic polymerization Of D,L-lactide using the oxyanion formed by reaction of the monohydroxyl monomethoxy-poly(ethylene glycol) on sodium hydride. For comparison, a similar copolymer was prepared by using tin octoate to catalyze the lactide polymerization. The copolymers were used to make nanoparticles, which were stored at 4 degrees C. After a few months under these storage conditions, a dramatic decrease of the poly(ethylene glycol) content was observed, however, the mean diameter of the nanoparticles was not affected. The degradation of the nanoparticles was investigated in vitro under conditions selected to mimic physiological conditions. Changes of characteristics were monitored by H-1 NMR, SEC, DLLS and CZE on nanoparticles and/or on the degradation by-products dissolved in the ageing medium. According to their nanometric dimensions, the microparticles degraded very slowly and there was no difference in behaviour between the sodium hydride and the stannous octoate-derived copolymers. (c) 2006 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据