JOURNAL OF NUCLEAR MATERIALS
卷 358, 期 1, 页码 40-46出版社
ELSEVIER
DOI: 10.1016/j.jnucmat.2006.06.010
关键词
-
The precipitation behaviour of the DIN 1.4970 steel and its effect on the intergranular corrosion resistance were studied. Time-temperature-precipitation diagrams for the secondary phases (Ti, Mo)C, (Cr, Fe, Mo, Ni)(23)C-6 and (Cr, Fe)(2)B are presented and representative samples have been selected for corrosion studies. The susceptibility to intergranular corrosion of the samples was evaluated using the double loop electrochemical potentiokinetic reactivation technique. The results showed that the solution-annealed samples and those aged at 1173 K did not present susceptibility to intergranular corrosion, whereas aging treatment from 873 to 1073 K resulted in small susceptibility to intergranular attack that decreased with aging temperature. The preferential formation of (Ti, Mo)C at higher aging temperatures comparatively to M23C6, retained the chromium in solid solution preventing steel sensitization and, consequently, intergranular corrosion. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据