期刊
CORROSION SCIENCE
卷 48, 期 12, 页码 4113-4126出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2006.03.005
关键词
Al-Li alloys; 8090; 7075; stress corrosion
The present paper focuses on the study of SCC behaviour of a new Al-Cu-Li alloy. For this purpose, two conventional media -NaCl and NaCl + H2O2 - were used for comparison with commercial alloys 7075 and 8090. This new alloy shows lower susceptibility to SCC than conventional alloys as it does not undergo environmentally-induced embrittlement in NaCl solutions and in 1 M NaCl + 0.3% H2O2 in which the 7075 and 8090 alloys, respectively, undergo environmentally-induced fracture. Solution composition was modified in order to determine the environmental conditions and strain rates under which this new alloy will crack due to a stress corrosion cracking phenomenon. The addition of 0.6 M sulphates to 1 M NaCl + 0.3% H2O2 solution allows the definition of a range of strain rate (between 10(-7) and 10(-6)s(-1)) in which this new alloy undergoes stress corrosion cracking. (c) 2006 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据