MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 438, 期 -, 页码 1124-1127出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2006.02.077
关键词
60Si2CrVA steel; isothermal transformation; low-temperature bainite; mechanical properties
A study is presented of the microstructures and mechanical properties of 60Si2CrVA steel subjected to isothermal transformation at 235 degrees C for 8 h and 270 degrees C for 3 h after austenizing at 1000 degrees C for 20 min. The microstructures of the steel after this treatment are composed of two phases, carbide-free bainitic ferrite and retained austenite, with lath- and film-like morphologies, respectively, and showing the features of low-temperature bainite. The corresponding mechanical properties are measured to be similar to 1980 MPa of tensile strength and similar to 9.5% of elongation for 235 degrees C-transformed sample, and similar to 1880 MPa and similar to 10.5% for 270 degrees C-transformed sample. The conventional lower bainite is not observed in the two isothermally transformed samples. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据