JOURNAL OF THE ELECTROCHEMICAL SOCIETY
卷 154, 期 1, 页码 D34-D37出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/1.2382346
关键词
-
Transparent conductive fluorine-doped tin oxide (FTO, SnO2: F) films were grown using a low-pressure metallorganic chemical vapor deposition (LP-MOCVD) with tetramethyltin (TMT), oxygen containing 2.96 mol % ozone (O-3), and hydrofluoric acid (HF) as a dopant. Using ozone contained oxygen instead of pure oxygen, the substrate temperature could be reduced by similar to 100 SC while maintaining a growth rate similar to that of tin oxide film. Growth rate of FTO film increased with the flow rate of TMT, however, adherence strength between the film and glass decreased. Resistivity of FTO thin films decreased with the TMT and HF flows over most of ranges investigated, while the resistivity increased rapidly with respect to excessive flow of the TMT over 300 sccm. Optical transmittance of FTO film was about 80% at 550 nm, and the variation as a function of HF flow rate was not significant. FTO film prepared at an optimum condition showed a minimum resistivity of 1.09 x 10(-3) Omega cm, a mobility of 19 cm(2)/Vs, and a carrier concentration of 3.05 x 10(20) cm(-3). (c) 2006 The Electrochemical Society.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据