Adhesion improvements of thermal barrier coatings with HVOF thermally sprayed bond coats

Thermal barrier coatings (TBC) are an effective engineering solution for the improvement of in service performance of gas turbines and diesel engine components. The quality and further performance of TBC, likewise all thermally sprayed coatings or any other kind of coating, is strongly dependent on the adhesion between the coating and the substrate as well as the adhesion (or cohesion) between the metallic bond coat and the ceramic top coat layer. The debonding of the ceramic layer or of the bond coat layer will lead to the collapse of the overall thermal barrier system. Though several possible problems can occur in coating application as residual stresses, local or net defects (like pores and cracks), one could say that a satisfactory adhesion is the first and intrinsic need for a good coating. The coating adhesion is also dependent on the pair substrate-coating materials, substrate cleaning and blasting, coating application process, coating application parameters and environmental conditions. In this work, the general characteristics and adhesion properties of thermal barrier coatings (TBCs) having bond coats applied using High Velocity Oxygen Fuel (HVOF) thermal spraying and plasma sprayed ceramic top coats are studied. By using HVOF technique to apply the bond coats, high adherence and high corrosion resistance are expected. Furthermore, due to the characteristics of the spraying process, compressive stresses should be induced to the substrate. The compressive stresses are opposed to the tensile stresses that are typical of coatings applied by plasma spraying and eventually cause delamination of the coating in operational conditions. The evaluation of properties includes the studies of morphology, microstructure, microhardness and adhesive/cohesive resistance. From the obtained results it can be said that the main failure location is in the bond coat/ceramic interface corresponding to the lowest adhesion values. (c) 2006 Elsevier B.V. All rights reserved.