期刊
ACS APPLIED MATERIALS & INTERFACES
卷 7, 期 8, 页码 4955-4961出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.5b00052
关键词
perovskite solar cells; polymer additive; morphology; coverage; solution process; TiO2 nanoparticle
资金
- National Science Council of Taiwan [MOST 103-3113-E-002-011]
Solution processable planar heterojunction perovskite solar cell is a very promising new technology for low cost renewable energy. One of the most common cell structures is FTO/TiO2/CH3NH3PbI3-xClx/spiro-OMeTAD/Au. The main issues of this type of solar cell are the poor coverage and morphology control of the perovskite CH3NH3PbI3-xClx film on TiO2. For the first time, we demonstrate that the problems can be easily resolved by using a polymer additive in perovskite precursor solution during the film formation process. A 25% increase in power conversion efficiency at a value of 13.2% is achieved by adding 1 wt % of poly(ethylene glycol) in the perovskite layer using a 150 degrees C processed TiO2 nanoparticle layer. The morphology of this new perovskite was carefully studied by SEM, XRD, and AFM. The results reveal that the additive controls the size and aggregation of perovskite crystals and helps the formation of smooth film over TiO2 completely. Thus, the V-oc and J(sc) are greatly increased for a high efficiency solar cell. The amount of additive is optimized at 1 wt % due to its insulating characteristics. This research provides a facile way to fabricate a high efficiency perovskite solar cell by the low temperature solution process (<150 degrees C), which has the advancement of conserving energy over the traditional high temperature sintering TiO2 compact layer device.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据