期刊
JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A
卷 80A, 期 2, 页码 333-341出版社
WILEY-LISS
DOI: 10.1002/jbm.a.30909
关键词
chemical coprecipitation; magnetite; sodium oleate; polyethylene glycol; nanoparticles; surfactant; cytotoxicity
In this study, magnetite (Fe3O4) nanoparticles with a size range of 8-20 nm were prepared by the modified controlled chemical coprecipitation method from the solution of ferrous/ferric mixed salt-solution in alkaline medium. In the process, two kinds of surfactant (sodium oleate and polyethylene glycol) were studied; then, sodium oleate was chosen as the apt surfactant to attain ultrafine, nearly spherical and well-dispersed (water-base) Fe3O4 nanoparticles, which had well magnetic properties. The size and size distribution of nanoparticles were determined by particle size analyzer. And the magnetite nanoparticles was characterized by X-ray powder diffraction (XRD) analysis, transmission electron microscopy (TEM), electron diffraction (ED) photography, Fourier transform infrared spectrometer (FT-IR), and vibrating-sample magnetometer (VSM). Also the effect of many parameters on the Fe3O4 nanoparticles was studied, such as reaction temperature, pH of the solution, stirring rate and concentration of sodium oleate. And the 5-dimethylthiazol-2-yl-2,5- diphenyltetrazolium bromide (MTT) assay was performed to evaluate the biocompatibility of magnetite nanoparticles. The results showed that the Fe3O4 nanoparticles coated by sodium oleate had a better biocompatibility, better magnetic properties, easier washing, lower cost, and better dispersion than the magnetite nanoparticles coated by PEG. (c) 2006 Wiley Periodicals, Inc. J Biomed Mater Res 80A: 333-341, 2007.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据