Cure behavior of unsaturated polyester/modified montmorillonite nanocomposites

Dynamic rheology, differential scanning calorimetry and in situ Fourier transform infrared spectroscopy were used to study the cure behavior of unsaturated polyester/modified montmorillonite nanocomposites. The results showed that their gel times increased markedly at the same cure temperature, and that the activation energy of the nanocomposites was higher than that of the pure unsaturated polyester. Their peak temperatures of enthalpy increased as well. The total exotherm. of the cure reaction declined and the cure rate decreased. In the curing process of pure unsaturated polyesters, the conversion of styrene was higher than that of the double bonds on unsaturated polyester macromolecular chains. The cure mechanism of the unsaturated polyester/modified montmorillonite changed because of the presence of double bonds in the layers of modified montmorillonite. However, the conversion of styrene in the nanocomposites was lower than that of double bonds on unsaturated polyester chains during cure at room temperature, and the conversion of styrene was increased after post-curing and was higher than that of the double bonds on unsaturated polyester chains at the end of the cure reaction. Moreover, the degree of reaction of double bonds on unsaturated polyester chains of the nanocomposites was higher than that of unsaturated polyesters. (c) 2006 Society of Chemical Industry.