期刊
JOURNAL OF POWER SOURCES
卷 164, 期 2, 页码 472-480出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jpowsour.2006.10.104
关键词
platinum nanoparticles; oleylamine; controlled size; heat treatment; catalytic activity; methanol oxidation
Well-dispersed Pt nanoparticles with controlled size and narrow size distribution were prepared by polyalcohol reduction of platinum acetylacetonate, using oleylamine as a capping agent. The particle size was varied from 3.5 nm to 11.5 nm by decreasing the amount of oleylamine added in the synthesis. Size selection of the as-prepared particles by solvent fractionation yielded nearly monodispersed Pt particles. The as-prepared particles were loaded on a carbon support by physical deposition, but showed no electrocatalytic activity due to the oleylamine bound to the particle surface. The particles were activated for electrocatalysis after heating the particles in air at 185 degrees C for 5 h, conditions that gave no particle-sintering and no oxidation. Cyclic voltammetry showed that the particles after the heat treatment in air were electrocatalytically active for methanol oxidation. The smaller 3.5 nm and 4.0 nm Pt particles had a higher intrinsic activity for methanol oxidation, but a lower tolerance to CO poisoning, compared with 6.0 nm, 9.5 nm and 11.5 nm particles. CO-stripping results suggest that CO is more easily oxidized on larger Pt particles. (c) 2006 Elsevier B.V All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据