期刊
TETRAHEDRON LETTERS
卷 48, 期 9, 页码 1553-1557出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.tetlet.2007.01.012
关键词
solubilization; polycondensation; polyimides; ionic liquids; Zwitterions
Three different ionic liquids were prepared and examined as solvents for polyimide synthesis. The solubility of 4,4'-oxy-dianiline and pyromellitic dianhydride as starting materials in ionic liquids was first evaluated, and then their polycondensation was carried out. Although these starting materials were hardly soluble in 1-benzyl-3-methylimidazolium bis(trifluoromethane sulfonyl)imide (3), addition of imidazolium type zwitterion, 1-(1-butyl-3-imidazolio)butane-4-sulfonate (ZI), certainly improved their solubility. When 3 containing 40 mol % ZI was used, nothing was phase separated from this mixed solution containing both starting materials after cooling down to room temperature. After preparing prepolymer in 3 containing 40 mol % of ZI at room temperature, polycondensation was carried out in the same solution at 100, 200, and then 300 degrees C for every 1 h to obtain polyimide. An inherent viscosity of the obtained polyimide (0.05 g in 10 ml concentrated sulfuric acid) was 1.3 dL g(-1), higher than that prepared in only 3 (0.9 dL g(-1)). The higher average molecular weight of the polyimide was attributed to the improved solubility of the starting materials by the addition of ZI that enabled the preparation of the prepolymer, poly(amide acid), without heating before imidation. (c) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据