CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY
卷 31, 期 1, 页码 141-147出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.calphad.2006.07.008
关键词
diffusion; gas phase; iron carbide; carburisation
Pure iron samples were carburised at 500 degrees C in CO-H-2-H2O-H2S gas mixtures to study the growth kinetics of metastable iron carbides. The carbon activity was varied in the range 7 <= a(C) <= 4580. Small amounts of H2S were added to the atmosphere to prevent graphite deposition and metal dusting from occurring. The gas composition was optimised to obtain parabolic carbide layer growth over a sufficiently long time period. At activities a(C) < 150 parabolic growth of cementite (Fe3C) was observed. At higher activities a(C) > 150 Hagg carbide (Fe5C2) formed on top of the cementite. From the dependence of the growth rate on carbon activity in the gas phase the self-diffusion coefficients D-C* of carbon at 500 degrees C were determined for both iron carbides Fe3C and Fe5C2. (c) 2006 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据