期刊
MATERIALS TRANSACTIONS
卷 48, 期 3, 页码 385-389出版社
JAPAN INST METALS & MATERIALS
DOI: 10.2320/matertrans.48.385
关键词
titanitun-gold; near-eutectoid alloy; aging; phase constitution; lattice parameter; mechanical properties
Effects of aging on phase constitution, lattice parameters and mechanical properties of Ti-4mol%Au near-eutectoid alloy were investigated. The alloy was fabricated by Ar arc-melting method, followed by homogenization at 1273 K for 3.6 ks. The ingot was cold-rolled with 95% reduction in thickness, solution treated at 1173 K for 0.9 ks and quenched into ice water. It was found that the apparent phase after the solution treatment was a supersaturated solid solution of a (hcp) phase. This supersaturated ce-phase is termed alpha(m) hereafter. The apparent phase of the aged alloys was a regardless of the aging temperature from 373 to 1073 K for 3.6 ks. The 0.2% flow stress was decreased as the aging temperature increased. On the other hand, by the isothermal aging at 973 K, Ti3Au with A15 structure was formed and the volume fraction of Ti3Au increased with increasing aging time. The 0.2% flow stress of the materials was decreased as the volume fraction of Ti3Au increased. This indicates that the Ti3Au precipitations are not effective on strengthening of the Ti-Au alloy.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据