DOI: 10.1016/j.jpowsour.2006.12.107
关键词
lithium batteries; LiMn2O4; lithium manganese spinel; template method; silica gel
A nanosized LiMn2O4 (nano-LiMn2O4) spinel was prepared by a novel route using a porous silica gel as a sacrificial hard template. This material was found to be made up of 8-20 nm nanoparticles with a mean crystallite size of 15 mn. The electrochemical properties of nano-LiMn2O4 were tested in lithium cells at different cycling rates and compared to those of microsized LiMn2O4 (micro-LiMn2O4) obtained by the classical solid state route. Microsized LiMn2O4 is formed by 3-20 mu m agglomerates, the size of each individual particle being approximately 0.20 mu m. The behaviour of nano-LiMn2O4 as a positive electrode improves with increasing current densities (from C/20 to 2C). Moreover, it was found to exhibit a noticeably better performance at high rates (2C), with higher initial capacity values and very good retention (only 2% loss after 30 cycles), with respect to micro-LiMn2O4, almost certainly due to enhanced lithium diffusion in the small particles. (c) 2007 Elsevier B.V All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据