DOI: 10.1016/j.msea.2006.10.136
关键词
bioactive glasses; crystallization; stoichiometry; microstructure
Devitrification treatment of Na2CaSi2O6-P2O5 based bioglasses (45S5.2 and 55S4.1) at 715 degrees C for up to 90 min caused amorphous phase separation via a bulk nucleation and growth mechanism, and then the formation of a single crystalline phase from the dispersed phosphorus-rich amorphous phase. The combined evidences of X-ray diffraction, optical/electron microscopy, energy dispersive X-ray analysis, Raman spectroscopy and density measurement indicated the crystal is approximately hexagonal in symmetry. Based on the isochemical crystallization of this phase from the 45S5.2 glass and the chemistry/density considerations, we suggested that the crystal is non-stoichiometric (Na-0.951 Ca-0.049)(2)Ca(Si0.899P0.101)(2)O-6. The 55S4.1 glass was partially crystallized as the same phase with relic SiO2-rich glass. The 45S5.2- or 55S4.1-based glass ceramics with tailored size and distribution of Na2CaSi2O6-type crystal may have potential applications as clinical implants. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据