DOI: 10.1016/j.apcatb.2006.06.013
关键词
Pt-Sn alloys; ethanol oxidation; direct ethanol fuel cells; thermal treatment
A carbon supported Pt-Sn electrocatalyst in the Pt:Sn atomic ratio 75:25 was prepared by the reduction of Pt and Sn precursors with formic acid and thermally treated at 200 degrees C (Pt-Sn200) and 500 degrees C (Pt-Sn500). Thermal treatment at both temperatures gave rise to the formation of a predominant phase of cubic Pt3Sn and, to a lesser extent, a hexagonal PtSn phase. The amount of the hexagonal PtSn phase as well as the particle size increased with increasing thermal treatment temperature. The formation of some very large particles (size > 30 nm) was apparent in the Pt-Sn500 catalyst. The activity for the ethanol oxidation reaction (EOR) and the performance in a single direct ethanol fuel cell (DEFC) of the catalyst thermally treated at 200 degrees C were better than both the as-prepared catalyst and Pt75Sn25/C by ETEK. The higher activity for the EOR of the Pt-Sn200 sample was ascribed to the presence of the Pt3Sn phase and to cleaning effect of the thermal treatment at 200 degrees C. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据