MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY
卷 139, 期 1, 页码 55-61出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.mseb.2007.01.034
关键词
solution combustion synthesis; CeAlO3; cerium oxides; solid-solid interfaces
Phase evolution of CeO2/gamma-Al2O3 system synthesized from single step solution combustion method is examined here. The nominal compositions of ceria and alumina in (CeO2)(x)/(Al2O3)(1-x) are varied from x = 0.0 to 0.66 to yield end compositions, gamma-Al2O3 to stoichiometric CeAlO3 phase. For the composition x = 0, the phase formed is gamma-Al2O3, and for x = 0.2, CeAlO3 is formed over gamma-Al2O3. As the cerium content increased beyond x = 0.2, CeO2/CeAlO3/gamma-Al2O3 oxides are formed. Heating CeAlO3/gamma-Al2O3 in air above 700 degrees C resulted in transformation to CeO2/gamma-Al2O3 and the subsequent reduction in H-2 gave back CeAlO3/gamma-Al2O3. TEM studies showed CeAlO3 crystallites growth on gamma-Al2O3 and the oxidized sample showed CeO2 formation over CeAlO3, which in turn interfaced with gamma-Al2O3 phase. XPS analysis of CeAlO3/gamma-Al2O3 phase showed the presence of Ce in +3 and +4 state indicating surface oxidized CeAlO3 phase. Epitaxial relation for growth of CeAlO3 over gamma-Al2O3 and CeO2 over CeAlO3 is demonstrated in the study, where adhesion of CeO2 over gamma-Al2O3 is via CeAlO3 phase at the interface. (c) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据