期刊
出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2006.11.054
关键词
superalloys; welding; HAZ cracking; liquid film migration
The heat affected zones (HAZs) of low and high heat input laser welds of a newly developed superalloy, ATI Allvac 718Plus, were studied. Low heat input welds suffered significant HAZ grain boundary liquation cracking, while no cracking was observed in spite of a more extensive HAZ intergranular liquation in the higher heat input welds. Combination of lower welding stresses generated during cooling, and relaxation of these stresses by thick intergranular liquid were suggested to be the factors that contributed to the absence of cracking in the high heat input welds. Further, healing of some of the HAZ cracks in lower heat input welds by fusion zone interdendritic liquid occurred through liquid backfilling. (c) 2006 Elsevier B.V. All rights reserved.