ELECTROCHEMISTRY COMMUNICATIONS
卷 9, 期 5, 页码 1077-1082出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.elecom.2006.12.013
关键词
lithium ion batteries; cathode materials; LiNi0.5Mn1.5O4; high-voltage; annealing treatment
High performance LiNi0.5Mn,O-1.5(4) was prepared by a combinational annealing method. All samples were characterized by X-ray diffraction, infrared, and cell measurements. With increasing the annealing time at 600 degrees C, LiNi0.5Mn1.5O4 showed a decreased lattice parameter and an enhanced Ni-ordering. The electrochemical property of LiNi0.5Mn1.5O4 was optimized by controlling the annealing time. It was found that after annealing at 600 degrees C for 8 h, LiNi0.5Mn1.5O4 can discharge up to 138 mA h g(-1) with a superior cycling performance at the rate of 5/7C. High-rate test indicated that. LiNi0.5Mn1.5O4 exhibited excellent electrochemical performance when charged and discharged at 1.2 C and 2.5 C, respectively. The findings reported in this work are expected to pave the way for the practical application of LiNi0.5Mn1.5O4. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据