Deep rolling of titanium rods for application in modular total hip arthroplasty

Compressive residual stresses are commonly introduced into the near-surface regions of morse taper junctions of modular hip endoprostheses to prolong fatigue life. An increasing number of publications report that contamination of shot-peened surfaces can lead to enhanced corrosion and third body wear. This study evaluates deep rolling of titanium alloy rods as a possible alternative to shot peening. Ten rods of Ti6Al7Nb alloy with a diameter of 15 mm were deep rolled with various rolling parameters. The resulting surface topography and residual contamination was analyzed using a scanning electron microscope (SEM). The near-surface residual stress states after deep rolling were characterized by means of X-ray diffraction. The roughness of the surfaces before deep rolling was about R-z = 14 mu m, and after deep rolling surface roughness values of R-z 0.4-7.5 mu m were achieved. The results of the SEM and EDAX analyses of the sample surface showed no evidence of surface contamination by particles or abrasion products caused by any process. At a pressure of 300 bar, compressive stress reached the maximum of -1150 MPa at a depth of 0.1 mm. Deep rolling thus allows a smooth and particle-free surface to be obtained and therefore shows promise as a surface treatment for mating surfaces of morse tapers in modular hip endoprostheses. (c) 2006 Wiley Periodicals. Inc.