microcapsules; phase change material; styrene-maleic anhydride; polyurethane; interfacial polycondensation
A series of polyurethane (PU) microcapsules containing a phase change material (PCM) of n-octadecane was successfully synthesized by an interfacial polymerization in aqueous styrene-maleic anhydride (SMA) dispersion with diethylene triamine (DETA) as a chain extender reacting with toluene-2,4-diisocyanate (TDI). Thermal analysis (TGA and DTA), FTIR, SEM, TEM measurements have been applied to analyze the properties of samples. The average diameter of microPCMs is in the range of 5-10 mu m under the stirring speed of 4000 rpm. Results showed that PU-shell regularly fabricated with the influence of SMA varied with weight ratio from 1.0 to 4.0% on diameter, encapsulated ratio, release properties and thermal stability. Also, the particle growth was controlled by the amount of SMA from measuring the shell thickness by SEM. However, the DSC curves of microPCMs samples prepared by 1.0, 2.0 and 3.0 wt.% of SMA indicated the thermal absorb-release property was not affected by the amount of the dispersant. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据